6061, 6082, 6063 Aluminum Sheet

Model NO.: 6061, 6082, 6063
Alloy: Alloy
Temper: T3 - T8
Certification: ASTM, JIS, GB/T
Sample: Free
Trademark: Baodi
Specification: SGS, ROHS
Origin: China
HS Code: 760612

Our plant was established in 1993 , with 20 years export Copper &Aluminum products experierence .
        Our main products as belows : 
        Copper Series : copper plate &sheet , copper strip , coppper pipe,copper rod , copper wire , cooper profile and so on. 
        Aluminum Series : pure sluminum plate &sheet , aluminum alloy plate&sheet , aluminum plate $sheet for moulding ,
       aluminum coil, aluminum tread plate, aluminum round rod , aluminum square bar , aluminum pipe , industrial aluminum profile and so on 
Specification Name: 6000 series Aluminum Sheet

Alloy: 6061, 6082, 6063 etc.

Temper: O, H112, T4, T6, T651 etc.

Thickness: 6-200mm

Width: Up to 1500mm

Surface treatment: mill finished, Print marks
Feature Machinability: In the harder T 4 and T6 tempers it is good. It is notably less easy to machine in the annealed temper.

Forming: Easily cold worked and formed in the annealed condition. Stamping, bending, spinning, deep drawing are all readily accomplished using standard methods.

Welding: It has very good welding characteristics and may be welded by all of the common welding techniques.

Heat Treatment: Solution heat treat at 990 F for adequate time to allow for thorough heating and then water quench. Precipitation hardening is done at 320 F for 18 hours and air cool, followed by 350 F for 8 hours and air cooling.

Forging: It is capable of being hot forged at temperatures in the range of 900 F to 750 F.

Hot Working: Hot working may be done in the temperature range of 700 F to 500 F.

Cold Working: Cold working in the O temper condition is readily performed. The alloy is notably less easy to cold form in the T 4 and T 6 tempers.

Annealing: Annealing should be done at 775 F for 2 to 3 hours followed by controlled cooling at 50 f per hour down to 500 F, then air cool.

Aging: The aging precipitation heat treatment is done at 350 F for 8 hours followed by air cooling. This produces the T6 temper.
Application Commonly used in the manufacture of heavy-duty structures requiring good corrosion resistance, truck and marine components, railroad cars, furniture, tank fittings, general structural and high pressure applications, wire products, pipelines, various toolings etc.
 
Alloy Chemical Component %≤

Si Fe Cu Mn Mg Cr Ni Zn Ti others Al










single total
6061 0.4- 0.8 0.7 0.15-0.4 0.15 0.8- 1.2 0.04-0.35 \ 0.25 0.15 0.05 0.15 remainder
6082 0.7- 1.3 0.5 0.1 0.4- 1.0 0.6- 1.2 0.25 \ 0.2 0.1 0.05 0.15 remainder
6063 0.2-
0.6
0.35 0.1 0.1 0.45-0.9 0.1 \ 0.1 0.1 0.05 0.15 remainder